Thermal expansion measurements were conducted on hot-pressed CrSi(sub 2), TiSi(sub 2), W Si(sub 2) and a two-phase Cr-Mo-Si intermetallic alloy between 293 and 1523 K during three heat-cool cycles. The corrected thermal expansion, (L/L(sub 0)(sub thermal), varied with the absolute temperature, T, as (deltaL/L(sub 0)(sub thermal) = A(T-293)(sup 3) + B(T-293)(sup 2) + C(T-293) + D, where A, B, C and D are regression constants. Excellent reproducibility was observed for most of the materials after the first heat-up cycle. In some cases, the data from the first heatup cycle deviated from those determined in the subsequent cycles. This deviation was attributed to the presence of residual stresses developed during processing, which are relieved after the first heat-up cycle. Raj, Sai V. Glenn Research Center NASA/TM-2014-216678, E-18874, GRC-E-DAA-TN13094
Publisher Name | Independently Published |
---|---|
Author Name | Hagendorf, Col |
Format | Audio |
Bisac Subject Major | SCI |
Language | NG |
Isbn 10 | 1794413464 |
Isbn 13 | 9781794413467 |
Target Age Group | min:NA, max:NA |
Dimensions | 01.10" H x 00.08" L x 50.00" W |
Page Count | 34 |
Write Your Own Review
Recommended Products
The Kite Runner 20th Anniversa...
Pre-order Price...
Regular Price
AED 140.00
Special Price
AED 93.00